Crusher Backing Compound
Our products are widely used in various industries

Crusher Backing Compound


Epoxy crusher backing compound is an ambient temperature curing, filler extended epoxy system used for the lining of cone crushers. The epoxy crusher backing compound is also suitable for the following ancillary applications: bonding, filling, fastening, or grouting of holding/fastening bolts.

Technical Information:

Product: Rotex  EP 64F Epoxy Crusher Backing Compound is a two part, ambient temperature curing, filler extended epoxy resin with good impact resistance and very low shrinkage.


ColourResin - Brown
Hardener Green
Mixing RatioBy Weight - 100 Parts resin : 6.25 parts hardener.
By Volume - 100 parts resin : 10 parts hardener.

Note:  Mix resin and hardener for 3 5 minutes. Use a spatula, or other flat-edged implement. Increase in temperature will shorten the working time, geltime and setting time. Decreases in temperature will extend the working time, geltime & setting time.

Specific Gravity@ 25 ºCMixed Compound 1.60 g/cm
Viscosity @ 25 ºCMixed Resin
Practical Working Time (Pot life)8.5 kg @ 25 ºC = 10 15 mts.

Typical Cured Properties:

Hardness after 24 hours@ 25ºCShore D 80 90
Shrinkage after CureMaximum 0.5 %.
Elongation (Average)1 %.
Tensile Strength250 300 kg/cm²
Compressive Strength700 900 kg/cm²
Heat Resistance- 10 to100
AdhesionTo Cleaned and roughened metal and concrete Excellent.

Chemical Resistance:  Excellent against water, oil, grease, detergents, diluted acids and alkaline. Resistant to solvents, aliphatic alcohols and aromatics. Against esters, ketones and chlorinated hydro-carbons, tests are recommended.

Water Absorption:  Immersion for 24 hrs @ 25ºC  in distilled water- maximum 2%.

Typical Properties: Easy Pourability and good penetration even at low temperatures. Minimal filler settlement in containers easily mixable. Fast reactivity and outstanding mechanical properties. Good curing properties at lower temperatures.

Crusher preparation:   Block all cracks or gaps in the lining between the crusher and steel lining. If no adhesion is required, apply a grease or silicon based release agent to the crusher bowl before casting.

Safety Precautions: Avoid direct contact of resin with skin. Use of hand gloves during handling is recommended. Splashes on the skin, if any should be removed immediately with suitable remover.

Note: The information given here reflects our present experience in development and usage. Since site conditions and situations vary, no warranty is given or responsibility assumed for obtaining specific technical results.

Transaction History of the Supplier

Below is the information about the supplier's transactions conducted via Alibaba.com. If you require further details regarding the transaction data, please contact the supplier directly.

Transaction Overview


Transaction Details

This supplier has completedtransactions with buyers from .

Shipping Destination
Transaction Value
Transaction Date
Email to this supplier
The supplier supports Trade Assurance – A free service that protects your orders from payment to delivery.
Supplier's Trade Assurance Limit: US $
Learn More